Materials Table
The range of available steel grades used by our company extends from general-purpose constructional steel over case hardening steel and tempering steel to corrosion- and acid resistant or highly heat-resistant steel. In close cooperation with the customer we suggest the ideal combination of materials according to the specific area of application. Trust us and you will benefit from our long years of experience when optimizing your chain.
Below is a list of the most common materials used in our workshop including standard hardness values. Of course, we also produce customer-specific from all available steel grades. Let us know your requirements and together we will find the best possible solution.
Material reference | Material No | Standard hardening | Standard hardening value | Standard hardening depth |
STANDARD QUALITIES | ||||
---|---|---|---|---|
C 15 | 1.0401 | Case hardening | 58-60 HRc | 0,8-1,0 mm |
C 45 | 1.0503 | Hardening and tempering | 800-900 N/mm² | Through |
20 Mn Cr 5 | 1.7147 | Case hardening | 58-60 HRc | 0,8-1,0 mm |
18 Cr Ni 8 | 1.5920 | Case hardening | 60-62 HRc | 0,8-1,0 mm |
42 Cr Mo 4 | 1.7225 | Hardening and tempering | 1100-1300 N/mm² | Through |
CORROSION- AND ACID-RESISTANT MATERIAL | ||||
X 5 Cr Ni 18-10 (V 2 A) | 1.4301 | - | ||
X 6 Cr Ni Mo Ti 17-12-2 (V 4 A) | 1.4571 | - | ||
X 46 Cr 13 | 1.4034 | Inductive hardening | 50-55 HRc | 1,5-2,0 mm |
X 39 Cr Mo 17-1 | 1.4122 | Inductive hardening | 49-52 HRc | 1,5-2,0 mm |
X 5 Cr Ni Cu Nb 16-4 | 1.4542 | Precipitation hardening | 410-470 HB | Through |
HIGHLY HEAT-RESISTANT | ||||
X 10 Cr Al Si 7 (up to 800°C) | 1.4713 | - | ||
X 15 Cr Ni Si 20-12 (up to 1200°C) | 1.4828 | - |
Material reference | Material No | Standard hardening | Standard hardening value | Standard hardening depth |
STANDARD QUALITIES | ||||
---|---|---|---|---|
16 Mn Cr 5 | 1.7131 | Case hardening | 58-60 HRc | 0,8-1,0 mm |
15 Ni Cr 13 (former 14 Ni Cr 14) | 1.5752 | Case hardening | 60-62 HRc | 0,8-1,0 mm |
18 Cr Ni 8 | 1.5920 | Case hardening | 60-62 HRc | 0,8-1,0 mm |
C 45 | 1.0503 | Inductive hardening | 58-62 HRc | 1,5-2,0 mm |
42 Cr Mo 4 | 1.7225 | Inductive hardening | 54-56 HRc | 1,5-2,0 mm |
CORROSION- AND ACID-RESISTANT MATERIAL | ||||
X 46 Cr 13 | 1.4034 | Inductive hardening | 50-55 HRc | 1,5-2,0 mm |
X 39 Cr Mo 17-1 | 1.4122 | Inductive hardeninig | 49-52 HRc | 1,5-2,0 mm |
X 105 Cr Mo 17 | 1.4125 | Inductive hardening | 60-62 HRc | 1,5-2,0 mm |
Material reference | Material No |
STANDARD QUALITIES | |
---|---|
S 235 JR (former St 37-2) | 1.0038 |
S 355 J2 (former St 52-3) | 1.0577 |
C 45 | 1.0503 |
Hardox | |
Creusabro | |
CORROSION- AND ACID-RESISTANT MATERIAL | |
X 5 Cr Ni 18-10 (V 2 A) | 1.4301 |
X 6 Cr Ni Mo Ti 17-12-2 (V 4 A) | 1.4571 |
HIGHLY HEAT-RESISTANT | |
X 10 Cr Al Si 7 (up to 800°C) | 1.4713 |
X 15 Cr Ni Si 20-12 (up to 1200 °C) | 1.4828 |
Material reference | Material No | Standard hardening | Standard hardening value |
STANDARD QUALITIES | |||
---|---|---|---|
C 67 S | 1.1231 | Hardening and tempering | 420-500 HV |
51 Cr V 4 | 1.8159 | Hardening and tempering | 410-500 HV |
CORROSION- AND ACID-RESISTANT MATERIAL | |||
X 10 Cr Ni 18-8 | 1.4310 | ||
X 46 Cr 13 | 1.4034 | Vacuum hardening | 42-49 HRc |
X 7 Cr Ni Al 17-7 | 1.4568 | Precipitation hardening | 400-480 HV |